Product Detail
Overview
Essential details
Place of Origin：Guangdong,China Brand Name：TINHU
Model Number：THS-1340C Color：Transparent
Mixing ratio：10:1 (by Weight) Features：High Tensile Strength
Usage：Screen Printing Viscosity：300000
Sample：Freely Samples MOQ：20KGS
Certificate：OEKO-TEX HS code：3910000000
Shelf life：1YEAR
Supply Ability
Supply Ability：20000 Kilogram/Kilograms per Day
Packaging & delivery
Packaging Details：100kg/bucket
20kg/bucket
200kg/bucket
Port：shenzhen port or guangzhou port
Picture Example：
Lead time：
| Quantity(kilograms) | 1 - 10000 | >10000 |
| Lead time (days) | 5 | To be negotiated |
Basic Info.
Model NO.
ths-1340c
| Material | Application | Certification | Trademark | Transport Package | Origin | HS Code | tensile strength(mpa) | elongation(%) | tear strength(kN/m) |
| Organic Silicone | Textile | REACH, RoHS | tinhu | 20kg/Bucket | China | 3910000000 | >6.5 | 350 | 9 |
Product Description
This is the embossed silicone rubber with high strength and easy to use.Our product is eco-friendy product,can contact with skin.
Silicone Rubber For Apparel Label THS-1340C
Features & Usage：
THS-1340C is an additional liquid silicone rubber with two components.It showed up good characteristics,such as excellent weatherability,dimensional stability,high transparency,avirulent environmental protection, high-adhesive strength,heatproof temperature exceeds 250C.It is widely used in printing of textile.
Technical parameters：
| Items | Data | |
| Before curing |
appearance(silicone/curing) | subtransparent/colorless viscous liquid |
| viscosity(silicone/curing)/mPa.s | 300000/500 | |
| Operation time(25ºC)/h | 5 | |
| After curing |
hardness/Shore A | 43 |
| density/g.cm-3 | 1.10 | |
| Tensile strength/MPa | 6.5 | |
| elongation/% | 350 | |
| Tear strength/kN.m-1 | 9 | |
| Shrinkage/% | 0.1 | |
Usage：
1.Mixture: Mix up silicone THS-1340C with curing agent according ratio 10:1.(If curing agent increased, the curing speed will get slower). Mixture can complete by hand or by equipment.
Package, storage & Notes：
1.Silicone package: 20KG/pail.Curing gent：2KG/tin
2.Keep it dry,ventilative and cool.To prevent the rain,sun exposure.
3.Avoid mixing curing agent of condensation silicone.Below also can influent curing effect,such as amine,sulfur compounds,phosphorus compound & melt salt. Avoiding moisture intrusion in using.
4.The products storage period about 1 year.Its fluidity can be recovered when intense agitation. We advised stir the silicone first then stir the silicone & curing agent mixture second.Expired products also can be used if passed re-inspection.
5.This products is a non-dangerous goods.
Applycation：
Printing on the back of the fabrics o get 3D embossed effect by heat mold after high frequency embossing machine.
Easy to release from the mold,high transparency,strong adhesion,excellent softness,no fall off after washing,no shape change.
There is no any color migration on PU/Rubber material.
The embossing pattern was lasting and natural on the leatherware which can save long printing effect.
Operation method：
The mix ratio is 10:1
Thinner adding ratio：10-40%,depends on fabric and embossing process
Heating temperature：150-190 degree
Normally the upside mold with temperature about 190 degree will better and downside mold with tem 150 degree.
Heating time：8-15 seconds,depends on the heating temperature.
Key Word:
附件下载:
Related Products
Dongguan tianhui new Material Co., Ltd.
Silicone Ink for Fabric Filling
Copyright © 2023 Dongguan tianhui new Material Co., Ltd. | SEO Powered by:www.300.cn dongguan.300.cn