Overview
Essential details
Place of Origin：Guangdong,China　　　Brand Name：TINHU
Model Number：THS-1340T　　　　　　　 Color：Transparent
Mixing ratio：10:1 (by Weight)　　　　Features：High Tensile Strength
Usage：Screen Printing　　　　　　　　Viscosity：200000
Sample：Freely Samples　　　　　　　　MOQ：20KGS
Certificate：OEKO-TEX　　　　　　　　 HS code：3910000000
Shelf life：1YEAR
Supply Ability
Supply Ability：20000 Kilogram/Kilograms per Day
Packaging & delivery
Packaging Details：100kg/bucket
　　　　　　　　　 20kg/bucket
　　　　　　　　　 200kg/bucket
Port：shenzhen port or guangzhou port
Picture Example：
Lead time：

Product Description
APPLICATION：
Quick Details
ace of Origin  Guangdong, China　　　　　Brand Name：tianhui tinhu
Model Number：THS-1340T　　　　　　　　　Application：The production of trademarks
Certificate：MSDS.ROHS.OCTEXT　　　　　　Advantage：Fast curing,strongadhesion,good
                       　　　　　　　　　　　　　　　　　　　　　flow performance
Hardness：42shore　　　　　　　　　　　　Appearance：Transparent
Mixing ratio：10:1　　　　　　　　　　　 MOQ：20 KGS
Shelf life：1 Year 2 Part Silicone　　　 Material：100% Silicone Material
Product name：Liquid Silicone Rubber For Label
Silicone Rubber For Textile THS-1340T
Features & Usage:
THS-1340Tis an additional liquid silicone rubber with two components. It showed up good characteristics, such as excellent weatherability, dimensional stability, high transparency, avirulent environmental protection, high-adhesive strength, heatproof temperature exceeds 250C. It is widely used in printing of textile.
Technical parameters:

Usage：
1.Mixture: Mix up silicone ThS-1340t with curing agent according ratio 10:1.(If curing agent increased, the curing speed will get slower). Mixture can complete by hand or by equipment.
2.Defoaming: Silicone mixture should be defoaming before printing on textile,the silicone volume will enlarge 1-5 times in vacuum. Please prepare 5times large vessel for defoaming.The mixtures will recover after a few minutes when stop defoaming,The defoaming has completed if no bulb comes out.
3.Moulding: The mixture will inject into mould use squeegee or dispensing process, then heating forming.
Package, storage & Notes：
1.Silicone package: 20KG/pail.Curing gent：2KG/tin
2.Keep it dry, ventilative and cool. To prevent the rain,sun exposure.
3.Avoid mixing curing agent of condensation silicone. Below also can influent curing effect, such as amine,sulfur compounds, phosphorus compound & melt salt.Avoiding moisture intrusion in using.
4.The products storage period about 1 year. Its fluidity can be recovered when intense agitation.We advised stir the silicone first then stir the silicone & curing agent mixture second. Expired products also can be used if passed re-inspection.
This products is a non-dangerous goods.
PROCESSER：
1. 1340T silicone mold pressure: curing agent mixed and stirred evenly at a ratio of 10:1(8 % in proportion to silica gel if the desired color is added)
After mixing evenly, fill the mold,clean the surface with a scraper, remove the vacuum, press the machine to spread the cloth, put the mold upside down on the cloth, and form it directly after press by the machine(the machine temperature is generally adjusted to 180-230 degrees,and the setting time is 20 seconds. About. Actual operation can be slightly adjust.
2.1340Tsilicone mold pressure: curing agent mixed and stirred evenly at a ratio of 10:1(8 % in proportion to silica gel if the desired color is added)
After mixing evenly, fill the mold, clean the surface with a scraper, remove the vacuum, press the machine to spread the cloth,put the mold upside down on the cloth, and form it directly after press by the machine(the machine temperature is generally adjusted to 180-230 degrees,and the setting time is 20 seconds. About.Actual operation can be slightly adjust.